BASF PA66 A3EG6 fiberglass reinforced 30% high rigidity heat-resistant engineering plastic raw material from Germany
Category:
Rubber and plastic/engineering plastic/PA66
Model:
A3EG6
Brand:
BASF
Filler content:
30% fiberglass
density:
1.37 g/cm³
water absorption rate:
2.5% (balanced)
tensile modulus:
8500 MPa
bending strength:
240 MPa
Heat Deflection Temperature:
250°C (1.8MPa)
Flame retardant rating:
HB
Place of Origin:
Germany
Retail Price
10,000,000.00USD
重量
kg
- Product Description
-
Filler content 30% fiberglass
density 1.37 g/cm³
water absorption rate 2.5% (balanced)
tensile modulus 8500 MPa
bending strength 240 MPa
Heat Deflection Temperature 250°C (1.8MPa)
Flame retardant rating HB
Place of Origin Germany
Description :
This PA66 A3EG6 is a classic modified nylon material produced by BASF in Germany. The core feature is the addition of 30% glass fiber for reinforcement. The addition of fiberglass significantly enhances the mechanical strength of the material. The tensile strength and bending modulus are much higher than those of pure PA66. Better dimensional stability and less likely to deform when heated. Suitable for manufacturing components with strict requirements for structural strength.
Heat resistance is another major advantage of this material. Continuous use at high temperatures, with excellent short-term temperature resistance. It can still maintain good physical properties in high temperature environments. The thermal deformation temperature has significantly increased, meeting the requirements of harsh working conditions. For application scenarios such as automotive engine peripheral components, electronic and electrical heat sinks, it can provide reliable long-term stability and reduce the risk of failure caused by thermal aging.
In terms of processing performance, A3EG6 has moderate fluidity and is easy to injection mold. Fast crystallization speed and short production cycle help improve production efficiency. Good surface glossiness and smooth appearance of the product. Although it contains fiberglass, it controls mold wear within a reasonable range. It is recommended to perform sufficient drying treatment before processing to prevent moisture from affecting the quality of the finished product. Conventional injection molding equipment is sufficient, with a wide process window and high operational error tolerance.
The application fields are very wide, commonly found in the automotive industry, electronic and electrical, and mechanical industries. Specific products include connectors, coil frames, switch components, gears, bearing cages, etc. These parts require high strength, high rigidity, and good heat resistance. Choosing BASF A3EG6 can ensure stable quality between batches. Abundant supply and standard specifications are commonly used materials for many injection molding and modification factories, and the cost-effectiveness is quite competitive among imported brands.