Impact resistant ABS Taiwan Chi Mei PA-757 high gloss

Description :

　　Impact resistant ABS Taiwan Chi Mei PA-757 high gloss

　　ABS PA757 has characteristics such as high rigidity, high gloss, and impact resistance.

　　Widely used: Home appliance/electronic/office product casing/copier casing/telephone casing/cosmetic container, etc

　　The body of the thermometer is usually made of Taiwan Qimei ABS757 raw material, which is harmless to the human body and has good formability and ultrasonic welding performance.

　　PA-757F Taiwan Chi Mei food contact grade ABS material has obtained low residual monomer (EU 10/2011 certification) and can provide ROHS, SGS, UL testing reports,

　　It can be used to manufacture food containers, portable water bottles, kitchenware products that come into contact with food, children's toys, etc. The processing conditions are divided into three aspects: drying conditions, injection machine sleeve temperature setting, and mold temperature.

　　ABS plastic is made by copolymerizing three types of monomers, and exhibits different properties with different contents. For example, with the increase of acrylonitrile content, it can effectively improve oil grade and chemical resistance. After being filled with butadiene, its toughness is increased. To achieve better processability, the proportion of styrene must be increased.

　　At present, there are many types of ABS on the market, which can be modified with additives to obtain various grades and performance products to meet the required performance requirements.

　　High performance ABS still relies on imports. Due to its low cost and extremely superior performance, it is widely used in various aspects of life, such as various ABS alloy shells, children's toys, low load bearings, refrigerator linings, and can be processed into various wear-resistant sheets and plates with good electrical performance.

　　Can be used as electronic components or automotive parts, various insulation materials, due to its easy surface processing, can be made into specified special products (such as electroplating), and is easy to color, can be processed into colorful products, and can also be used as fireproof electrical enclosures, alloy to improve its comprehensive performance

　　POLYLAC® PA-757 Taiwan Qimei ABS Physical Property Table

　　Features include:

　　Flame retardant/rated flame

　　Obtained ROHS certification

　　Physical properties rated value system of units test method

　　specific gravity

　　-- 1.05 g/cm3

　　23°C 1.05 g/cm3 ISO 1183

　　Melt flow rate

　　200°C/5.0 kg 1.6 g/10 min

　　220°C/10.0 kg 22 g/10 min

　　Dissolved Volume Flow Rate (MVR) (220 ° C/10.0 kg) 22.0 cm3/10 min ISO 1133

　　hardness rated value system of units test method

　　Rockwell hardness (R grade) 116

　　thermal performance rated value system of units test method

　　Thermal deformation temperature under load

　　1.8 MPa, Unanealed at 85.0 ° C

　　1.8 MPa, Unanealed 88.0 ° C ISO 75-2/A

　　1.8 MPa, Annealing at 95.0 ° C

　　1.8 MPa, Annealing at 98.0 ° C ISO 75-2/A

　　Vicat softening temperature

　　-- 105 °C

　　-- 104 °C ISO 306/A50

　　-- 100 °C ISO 306/B50

　　flammability rated value test method

　　UL flame retardant rating (1.60 mm) HB UL 94