Low viscosity PC 2405 Shanghai Covestro General Industrial Automotive Raw Material
Category:
Rubber and plastic/engineering plastic/PC
Model:
Brand:
Shanghai Bayer
Retail Price
20.00USD
重量
kg
- Product Description
-
Description :
PC 2405 Shanghai Covestro
Basic Information
Characteristic low viscosity
General
Good demolding performance
Universal use
RoHS Compliance RoHS Compliance
Appearance semi transparent
opaque
Available colors
Clear/Transparent
Processing method: Injection molding
2405 Physical Property Table
Physical performance rating unit testing method
Density (23 ° C) 1.20 g/cm3 ISO 1183
Apparent density 1 0.66 g/cm3 ISO 60
Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 20 g/10 min ISO 1133
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 19.0 cm3/10 min ISO 1133
shrinkage rate
Vertical flow direction 0.50 to 0.70% ISO 2577
Flow direction 0.50 to 0.70% ISO 2577
Vertical flow direction: 2.00 mm 2 0.70% ISO 294-4
Flow direction: 2.00 mm 3 0.65% ISO 294-4
Water absorption rate ISO 62
Saturation, 23 ° C 0.30% ISO 62
Balance, 23 ° C, 50% RH 0.12% ISO 62
Test method for hardness rating unit system
Ball compression hardness 115 MPa ISO 2039-1
Mechanical performance rating unit testing method
Tensile modulus (23 ° C) 2400 MPa ISO 527-2/1
Tensile stress ISO 527-2/50
Yield, 23 ° C 65.0 MPa ISO 527-2/50
Fracture, 23 ° C 65.0 MPa ISO 527-2/50
Tensile strain ISO 527-2/50
Yield, 23 ° C 6.0% ISO 527-2/50
Fracture, 23 ° C 130% ISO 527-2/50
Nominal tensile fracture strain (23 ° C)>; 50 % ISO 527-2/50
Tensile creep modulus ISO 899-1
1 hr 2200 MPa ISO 899-1
1000 hr 1900 MPa ISO 899-1
Bending modulus 4 (23 ° C) 2350 MPa ISO 178
Bending stress 5 ISO 178
3.5% strain, 23 ° C 73.0 MPa ISO 178
23°C 97.0 MPa ISO 178
Flexural Strain at Flexural Strength (23°C) 6 7.1 % ISO 178
Test Method for Film Rating Unit System
Gas Permeation ISO 2556
Carbon Dioxide : 23°C, 25.4 μm 18900 cm3/m2/bar/24 hr ISO 2556
Carbon Dioxide : 23°C, 100.0 μm 4000 cm3/m2/bar/24 hr ISO 2556
Nitrogen : 23°C, 25.4 μm 630 cm3/m2/bar/24 hr ISO 2556
Nitrogen : 23°C, 100.0 μm 130 cm3/m2/bar/24 hr ISO 2556
Oxygen : 23°C, 25.4 μm 3150 cm3/m2/bar/24 hr ISO 2556
Oxygen : 23°C, 100.0 μm 700 cm3/m2/bar/24 hr ISO 2556
Test method for flammability rating unit system
Application of Flame from Small Burner - Method K and F (2.00 mm) K1, F1 DIN 53438-1, -3
Burning Rate - US-FMVSS (> 1.00 mm) passed ISO 3795
Flash Ignition Temperature 480 °C ASTM 1929
Needle Flame Test IEC 60695-11-5
Method F
AfterSalesService :
Key words:- Low viscosity PC