High rigidity PC G-3420H Japanese Teijin anti creep low anisotropy
Panlite® G-3420H Physical Properties Table
Filler/reinforcement material glass fiber reinforcement material, 20% filler by weight
Characteristics: low anisotropy rigidity, high and good creep resistance
Usage: Industrial Applications, Camera Applications
Formal particle
Processing method: Injection molding
Physical performance rating unit testing method
Density 1.34 g/cm3 ISO 1183
Internal method of shrinkage rate
Vertical flow direction: 4.00 mm 0.40 to 0.60% internal method
Flow direction: 4.00 mm 0.20 to 0.40% internal method
Water absorption rate (23 ° C, 24 hr) 0.14% ISO 62
Mechanical performance rating unit testing method
Tensile modulus 5000 MPa ISO 527-2/1
Tensile stress (fracture) 85.0 MPa ISO 527-2/5
Tensile strain (fracture) 3.0% ISO 527-2/5
Bending modulus 1 5000 MPa ISO 178
Bending stress 2 135 MPa ISO 178
Test method for impact performance rating unit system
Impact strength of simply supported beam with notch 9.0 kJ/m2 ISO 179
Simply supported beam without notch impact strength 58 kJ/m2 ISO 179
Test method for thermal performance rating unit system
Heat Deflection Temperature
0.45 MPa, Unanealed 143 ° C ISO 75-2/B
1.8 MPa, Unanealed 137 ° C ISO 75-2/A
Vicat softening temperature 146 ° C ISO 306/B50
Linear coefficient of thermal expansion ISO 11359-2
Flow 4.0E-5 cm/cm/° C ISO 11359-2
Horizontal 6.0E-5 cm/cm/° C ISO 11359-2
RTI Elec (1.50 mm) 130 °C UL 746
RTI Imp (1.50 mm) 125 °C UL 746
RTI (1.50 mm) 130 °C UL 746