Friction resistant PC LS-1250 Japanese Teijin Wear resistant

Description :

　　Friction resistant PC LS-1250 Japanese Teijin Wear resistant

　　LS-1250 PC | Polycarbonate # Adhesive Japanese Emperor

　　Product use: Used for components with requirements for friction and wear resistance.

　　Note: Characteristics: Friction resistant type.

　　LS-1250 Physical Property Table

　　Basic performance rating unit testing method

　　Water absorption rate (24 hours in water at 23 ° C) 0.17% ASTM -570

　　Physical performance rating unit testing method

　　Specific gravity 1.26 ASTM 792

　　Flame retardant UL 94

　　(Thickness 1.47mm) 94V-2

　　(Thickness 3.05mm) 94V-1

　　Transmittance (thickness 3mm) Translucent% ASTM -1003

　　Mechanical performance rating unit testing method

　　Bending strength 78 (800) Mpa (kgf/cm) ASTM 790

　　Tensile strength ASTM 638

　　Impact strength value (with a notch thickness of 6.4mm) 120 (12) j/m (kgf · cm/cm) ASTM 256

　　Tensile modulus 2300 (23500) Mpa (kgf/cm) ASTM 6

　　Rockwell hardness 67 M scale ASTM 785

　　Impact strength value (with a notch thickness of 3.2mm) 290 (30) j/m (kgf · cm/cm) ASTM 256

　　Bending modulus 2110 (21500) Mpa (kgf/cm) ASTM 790

　　Compressive strength 73 (740) Mpa (kgf/cm) ASTM 695

　　Tensile strength ASTM 638

　　55(560) Mpa(kgf/cm)

　　51(520) Mpa(kgf/cm)

　　Insulation breaking strength (rapid pressure value thickness 1.6mm) 30 KV/mm ASTM 149