Polycarbonate PC Korea Lotte SC-1220R Universal Grade
PC Korea Lotte SC-1220R
You can directly call for consultation on issues such as high gloss black PC and Apple white PC.
1、 Product Introduction
Polycarbonate 3.1 Introduction Polycarbonate is an odorless, odorless, non-toxic, and transparent amorphous thermoplastic material. It is a general term for a class of high molecular weight compounds containing carbonates in their molecular chains, abbreviated as PC. The general structural formula can be expressed, and due to the different R groups, it can be divided into two types: aliphatic and aromatic. However, due to limitations in product performance, processing performance, and economic factors, only bisphenol A-type aromatic polycarbonate has been put into industrial scale production and application. Bisphenol A-type polycarbonate is currently the most widely produced and used polycarbonate, and also one of the fastest developing engineering plastics. BisphenolA type Polycarbonate (PC) is widely used in electrical and electronic parts, mechanical textile industrial parts, building structural parts, aviation transparent materials and parts, foam structural materials, etc. due to its excellent impact strength, creep resistance, heat and cold resistance, aging resistance, electrical insulation and light transmittance.
2、 Product parameters
Physical Property Table of PC Korea Lotte SC-1220R
Physical performance rating unit testing method
Specific gravity 1.22 g/cm3
Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 18 g/10 min
Test method for hardness rating unit system
Rockwell hardness R grade 120 R scale 120 ISO 2039-2
Mechanical performance rating unit testing method
tensile strength
Yield 1 59.0 MPa
Yield 63.0 MPa ISO 527-2/5
flexural modulus
-- 2 2200 MPa
-- 3 2260 MPa ISO 178
bending strength
-- 4 83.0 MPa
-- 5 90.0 MPa ISO 178
Test method for impact performance rating unit system
Simply supported beam notch impact strength 6 (23 ° C) 60 kJ/m2 ISO 179/1eA
Impact strength of cantilever beam gap
23 ° C, 3.18 mm without fracture (flexibility failure)
23°C 7 65 kJ/m2 ISO 180/1A
Test method for thermal performance rating unit system
Hot deformation temperature (1.8 MPa, unannealed, 4.00 mm) 125 ° C ISO 75-2/A
Vicat softening temperature 140 ° C ISO 306/B50
Flammability rating test method
UL flame retardant rating UL 94
0.800 mm V-2 UL 94
3.20 mm V-2 UL 94