Low viscosity PC from Covestro Germany Rx1452 medical device raw material
Category:
Rubber and plastic/engineering plastic/PC
Model:
Brand:
Bayer Germany
Retail Price
42.00USD
重量
kg
- Product Description
-
Description :
Low viscosity PC from Covestro Germany Rx1452 medical device raw material
Our company supplies medical polymer materials from brands such as SABIC and Covestro. For inquiries about raw materials such as PE, PEI, PC, PP, etc., please click on the "Call" button below for free consultation!
Makrolon® Rx1452 Physical Property Table
Low viscosity and good demolding performance
Usage: Medical/nursing supplies, medical devices
Processing method: Injection molding
Physical properties rated value system of units test method
Density (23 ° C) 1.20 g/cm3 ISO 1183
Apparent density 1 0.66 g/cm3 ISO 60
Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 17 g/10 min ISO 1133
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 16.0 cm3/10 min ISO 1133
shrinkage rate
Vertical flow direction 0.60 to 0.80% ISO 2577
Flow direction 0.60 to 0.80% ISO 2577
Vertical flow direction: 280 ° C, 2.00 mm 2 0.70% ISO 294-4
Flow direction: 280 ° C, 2.00 mm 3 0.70% ISO 294-4
Water absorption rate ISO 62
Saturation, 23 ° C 0.30% ISO 62
Balance, 23 ° C, 50% RH 0.12% ISO 62
hardness rated value system of units test method
Ball hardness 118 MPa ISO 2039-1
mechanical properties rated value system of units test method
Tensile modulus (23 ° C) 2400 MPa ISO 527-2/1
Tensile stress ISO 527-2/50
Yield, 23 ° C 68.0 MPa ISO 527-2/50
Fracture, 23 ° C 70.0 MPa ISO 527-2/50
Tensile strain ISO 527-2/50
Yield, 23 ° C 6.0% ISO 527-2/50
Fracture, 23 ° C 130% ISO 527-2/50
Nominal tensile fracture strain (23 ° C)>; 50 % ISO 527-2/50
Bending modulus 4 (23 ° C) 2400 MPa ISO 178
Bending stress 5 ISO 178
3.5% strain, 23 ° C 78.0 MPa ISO 178
23°C 100 MPa ISO 178
Flexural Strain at Flexural Strength 6(23°C) 6.8 % ISO 178
flammability rated value system of units test method
Flash Ignition Temperature 480 °C
Self Ignition Temperature 550 °C
Supplementary Information Rating
ISO Shortname ISO 7391-PC
impact performance rated value system of units test method
Simply supported beam without notch impact strength ISO 179/1eU
-30 ° C without fracture ISO 179/1eU
23 ° C without fracture ISO 179/1eU
Suspended wall beam notch impact strength 7 ISO 7391
-30 ° C, complete fracture 12 kJ/m2 ISO 7391
23 ° C, local fracture 65 kJ/m2 ISO 7391
Multi axis Instrumented Impact Energy ISO 6603-2
-30°C 65.0 J ISO 6603-2
23°C 60.0 J ISO 6603-2
Multi axis Instrumented Peak Impact Force ISO 6603-2
-30°C 6200 N ISO 6603-2
23°C 5300 N ISO 6603-2
thermal performance rated value system of units test method
Heat Deflection Temperature
0.45 MPa, Unanealed 132 ° C ISO 75-2/B
1.8 MPa, Unanealed 120 ° C ISO 75-2/A
Vicat softening temperature
-- 140 °C ISO 306/B50
-- 141 °C ISO 306/B120
Ball Pressure Test (132°C) Pass IEC 60695-10-2
Linear coefficient of thermal expansion ISO 11359-2
Flow: 23 to 55 ° C 6.5E-5 cm/cm/° C ISO 11359-2
Horizontal: 23 to 55 ° C 6.5E-5 cm/cm/° C ISO 11359-2
Thermal conductivity 8 (23 ° C) 0.20 W/m/K ISO 8302
optical performance rated value system of units test method
Transmittance (3000 μ m) 86.0% ISO 13468-2
Haze (3000 μ m) 1.0% ISO