PC resin HP1 Sabouraud based high flow pharmaceutical material
Category:
Rubber and plastic/engineering plastic/PC
Model:
Brand:
Basic Innovative Plastics&# 40; United States&# 41
Retail Price
50.00USD
重量
kg
- Product Description
-
Description :
PC resin HP1 Sabouraud based high flow pharmaceutical material
HP1 color code: HP1-1H112, etc. can be consulted directly
LEXAN? HP1 Resin Physical Properties Table
Additive demolding
Characteristics: Ethylene oxide disinfection, high fluidity, high biocompatibility
Usage: Pharmaceuticals, Medical/Nursing Supplies
Processing method: Injection molding
Physical properties rated value system of units test method
specific gravity
-- 1.20 g/cm3
-- 1.19 g/cm3
Specific volume 0.835 cm3/g
Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 25 g/10 min
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 23.5 cm3/10 min ISO 1133
Shrinkage rate - flow (3.20 mm) 0.50 to 0.70% internal method
water absorption rate
24 hr 0.15 %
Balance, 23 ° C 0.35%
Balance, 100 ° C 0.58%
hardness rated value system of units test method
Rockwell hardness
M-grade 70
R-grade 118
mechanical properties rated value system of units test method
tensile modulus
-- 1 2380 MPa
-- 2350 MPa ISO 527-2/1
tensile strength
Yield 2 62.1 MPa
Yield 63.0 MPa ISO 527-2/50
Fracture 3 65.5 MPa
Fracture 50.0 MPa ISO 527-2/50
elongation
Yield 4 6.0%
Yield 6.0% ISO 527-2/50
Fracture 5 120%
Fracture 70% ISO 527-2/50
flexural modulus
50.0mm span 6 2310 MPa
-- 7 2300 MPa ISO 178
bending stress
-- 90.0 MPa ISO 178
Yield, 50.0mm span 8 93.1 MPa
Taber Wear Resistance (1000 Cycles, 1000 g, CS-17 Wheel) 10.0 mg
impact performance rated value system of units test method
Simply supported beam notch impact strength 9 ISO 179/1eA
-30°C 10 kJ/m2 ISO 179/1eA
23°C 12 kJ/m2 ISO 179/1eA
Impact strength of cantilever beam gap
Colors 110 to 640 J/m
Natural, Tints 640 J/m
-30°C 10 10 kJ/m2 ISO 180/1A
23°C 11 12 kJ/m2 ISO 180/1A
Non notched cantilever beam impact
23°C 3200 J/m
-30 ° C 12 without fracture ISO 180/1U
23 ° C 13 fracture free ISO 180/1U
Dart impact equipped with measuring instruments (23 ° C, Energy at Peak Load) 54.2 J
Hammer impact (23 ° C) 169 J
Tensile impact strength 14 378 kJ/m2
thermal performance rated value system of units test method
Thermal deformation temperature under load
0.45 MPa, Unanealed, 6.40 mm, 138 ° C
0.45 MPa, Unanealed, 100mm span 15 133 ° C ISO 75-2/Be
1.8 MPa, Unanealed, 6.40 mm, 127 ° C
1.8 MPa, Unanealed, 100mm span 16 121 ° C ISO 75-2/Ae
Vicat softening temperature
-- 139 °C ISO 306/B50
-- 140 °C ISO 306/B120
Ball Pressure Test (125°C) Pass IEC 60695-10-2
Linear coefficient of thermal expansion - flow
-40 to 95 ° C 6.8E-5 cm/cm/° C
23 to 80 ° C 7.0E-5 cm/cm/° C ISO 11359-2
Specific heat 1260 J/kg/° C
thermal conductivity
-- 0.19 W/m/K
-- 0.20 W/m/K ISO 8302
RTI Elec 130 °C UL 746
RTI Imp 130 °C UL 746
RTI 130 °C UL 746
Electrical performance rated value system of units test method
Surface resistivity>1.0E+15 ohms IEC 60093
volume resistivity
-- > 1.0E+17 ohms·cm
-- > 1.0E+15 ohms·cm IEC 60093
dielectric strength
3.20 mm, in Air 15 kV/mm
3.20 mm, 17 kV/mm IEC 60243-1 in oil
dielectric constant
50 Hz 3.17
60 Hz 3.17
1 MHz 2.96
50 Hz 2.70 IEC 60250
60 Hz 2.70 IEC 60250
1 MHz 2.70 IEC 60250
Dissipation factor
50 Hz 9.0E-4
60 Hz 9.0E-4
1 MHz 0.010
50 Hz 1.0E-3 IEC 60250
60 Hz 1.0E-3 IEC 60250
Compared to the Leakage Traceability Index (CTI) PLC 2 UL 746
High Arc Ignition Index (HAI) PLC 1 UL 746
High Voltage Arc Traceability Rate (HVTR) PLC 2 UL 746
Hot wire ignition (HWI) PLC 2 UL 746
flammability rated value system of units test method
UL flame retardant rating (1.09 mm) V-2 UL 94
Extreme Oxygen Index 25% ISO 4589-2
optical performance rated value system of units test method
Refractive index 1.586
Transmittance (2540 μ m) 88.0%
Haze (2540 μ m) 1.0%
injection rated value system of units
Drying temperature 121 ° C
Drying time 3.0 to 4.0 hours
Drying time 48 hours
Suggested moisture content of 0.020%
Suggested injection volume of 40 to 60%
The temperature at the rear of the barrel is 249 to 271 ° C
The temperature in the middle of the barrel is 260 to 282 ° C
The temperature at the front of the barrel ranges from 271 to 293 ° C
Spray nozzle temperature 266 to 288 ° C
Processing (melt) temperature 271 to 293 ° C
Mold temperature ranging from 71.1 to 93.3 ° C
Back pressure ranging from 0.345 to 0.689 MPa
Screw speed 40 to 70 rpm
Exhaust hole depth 0.025 to 0.076 mm