UV resistant PC Mitsubishi S-3000UR 5355 Transparent and Steam resistant

Description :

　　UV resistant PC Mitsubishi S-3000UR 5355 Transparent

　　Excluding UV PC S-3000R

　　PC S-3000UR 5313 blue background white

　　Mitsubishi in Thailand, Mitsubishi in Japan, and Mitsubishi in Shanghai can directly connect to the power grid if needed!

　　ASTALON? S3000UR Physical Properties Table

　　Basic Information Additive demolding UV stabilizer

　　feature Low viscosity processability, good flowability, high heat resistance, moderate toughness, good universality, moderate transparency, flame retardancy

　　purpose Application of safety equipment in the automotive field: universal shell

　　processing method injection molding

　　Physical properties rated value system of units test method

　　Specific gravity 1.20 g/cm3

　　Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 18 g/10 min

　　Shrinkage - Flow (3.00 mm) 0.60%

　　Water absorption rate (24 hours) 0.24%

　　hardness rated value system of units test method

　　Rockwell hardness (R grade) 123

　　mechanical properties rated value system of units test method

　　Tensile strength 1 (3.20 mm) 63.0 MPa

　　Elongation rate 2 (fracture, 3.20 mm) 110%

　　Bending modulus 3 (6.40 mm) 2350 MPa

　　Bending strength 4 (6.40 mm) 88.0 MPa

　　impact performance rated value system of units test method

　　Suspended wall beam notch impact strength (3.20 mm) 830 J/m

　　Falling hammer impact (3.20 mm)> 85.0 J

　　thermal performance rated value system of units test method

　　Thermal deformation temperature under load

　　0.45 MPa, Unanealed, 6.40 mm, 152 ° C

　　1.8 MPa, Unanealed, 6.40 mm, 137 ° C

　　Linear thermal expansion coefficient - flow 6.5E-5 cm/cm/° C

　　Electrical performance rated value system of units test method

　　Volume resistivity 2.1E+16 ohms · cm

　　Dielectric constant 2.85

　　flammability rated value system of units test method

　　UL flame retardant rating (1.60 mm) V-2 UL 94

　　optical performance rated value system of units test method

　　Transmittance (total, 3000 μ m) 85.0%

　　injection rated value system of units

　　Drying temperature 120 to 125 ° C

　　Drying time 4.0 to 6.0 hours

　　The temperature at the rear of the barrel is 235 to 265 ° C

　　The temperature in the middle of the barrel is 250 to 270 ° C

　　The temperature at the front of the barrel is 265 to 285 ° C

　　Processing (melt) temperature 260 to 290 ° C

　　Mold temperature 60.0 to 110 ° C

　　Injection pressure ranging from 60.0 to 140 MPa

　　Moderate injection speed

　　Back pressure ranging from 0.100 to 0.500 MPa

　　Screw speed 40 to 60 rpm

　　Locking force 4.0 to 8.0 kN/cm2