Opaque PC PC-110N Taiwan Chi Mei Automotive Application
Category:
Rubber and plastic/engineering plastic/PC
Model:
Brand:
Taiwan Qimei
Retail Price
23.00USD
重量
kg
- Product Description
-
Description :
PC PC-110N Taiwan Chi Mei
Opaque, flame retardant, mainly used for applications in the automotive industry
PC-110N Polycarbonate Flame Retardant Physical Properties Table
Physical properties Rated value (metric) Rated Value (Imperial System) test method density 1.20 g/cc 0.0434 lb/in3 ISO 1183 Melt flow rate 13 g/10 min@Load 1.20 kg, Temperature 300 °C 13 g/10 min@Load 2.65 lb, Temperature 572 °F Melt Volume Rate (ml/10 min); ISO 1133 mechanical properties Rated value (metric) Rated Value (Imperial System) test method Ball pressure hardness 100 MPa 14500 psi H358/30; ISO 2039-1 Tensile strength (fracture) 75.0 MPa 10900 psi 50 mm/min; ISO 527 Tensile strength (yield) 65.0 MPa 9430 psi 50 mm/min; ISO 527 Elongation (fracture) 120 % 120 % 50 mm/min; ISO 527 bending strength 90.0 MPa 13100 psi 2 mm/min; ISO 178 flexural modulus 2.40 GPa 348 ksi 2 mm/min; ISO 178 Impact strength of cantilever beam gap 80.0 kJ/m2 38.1 ft-lb/in2 ISO 180/4A Charpy Notched Impact Strength 7.50 J/cm2 35.7 ft-lb/in2 ISO 179 thermal performance Rated value (metric) Rated Value (Imperial System) test method Thermal deformation temperature under load (1.8 MPa) 127 °C 261 °F annealed; ISO 75 142 °C 288 °F unannealed; ISO 75 Vicat softening temperature 143 °C@Load 5.00 kg 289 °F@Load 11.0 lb 50°C/hr; ISO 306 148 °C@Load 1.00 kg 298 °F@Load 2.20 lb 50°C/hr; ISO 306 Flammability (UL94) V-2@Thickness 1.50 mm V-2@Thickness 0.0590 in AfterSalesService :
Key words:- Opaque PC