Automotive parts PC PC-110L Taiwan Chi Mei flame retardant and weather resistant
Category:
Rubber and plastic/engineering plastic/PC
Model:
Brand:
Taiwan Qimei
Retail Price
29.80USD
重量
kg
- Product Description
-
Description :
PC PC-110L Taiwan Chi Mei
Features include:
Flame retardant/rated flame, weather resistant
Obtained ROHS certification
Purpose: Application in the automotive field
PC-110L Physical Properties Table
Basic Information
Yellow card number E56070-100239153
Application in the field of automobiles
RoHS Compliance RoHS Compliance
Processing method: Injection molding
Physical performance rating unit testing method
Specific gravity 1.20 g/cm3 ASTM 792, ISO 1183
Melt flow rate (300 ° C/1.2 kg) 10 g/10 min ASTM 1238
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 10.0 cm3/10 min ISO 1133
Shrinkage rate ASTM 955
Flow rate of 0.50 to 0.70% ASTM 955
Lateral flow 0.50 to 0.70% ASTM 955
Water absorption rate (23 ° C, 24 hr) 0.20% ASTM 570
Test method for hardness rating unit system
Rockwell hardness (M grade) 77 ASTM 785
Ball indentation hardness (H 358/30) 100 MPa ISO 2039-1
Mechanical performance rating unit testing method
tensile strength
Yield, 3.18 mm 1 61.8 MPa ASTM638
Yield 65.0 MPa ISO 527-2/50
Fracture 75.0 MPa ISO 527-2/50
elongation
Yield, 3.18 mm 2 6.0% ASTM 638
Fracture, 3.18 mm 3 110% ASTM 638
Fracture 120% ISO 527-2/50
flexural modulus
6.35 mm 4 2350 MPa ASTM 790
-- 5 2400 MPa ISO 178
bending strength
6.35 mm 6 90.2 MPa ASTM 790
-- 7 90.0 MPa ISO 178
Compressive strength 76.5 MPa ASTM 695
Test method for impact performance rating unit system
The impact strength of a simply supported beam with a notch is 75 kJ/m2 according to ISO 179
Impact strength of cantilever beam gap
3.18 mm 850 J/m ASTM 256
-- 80 kJ/m2 ISO 180/1A
Test method for thermal performance rating unit system
Thermal deformation temperature under load
0.45 MPa, Unanealed 8 136 ° C ASTM 648
1.8 MPa, Unanealed 9 125 ° C ASTM 648
1.8 MPa, Unanealed 127 ° C ISO 75-2/A
1.8 MPa, Annealing at 142 ° C ISO 75-2/A
Vicat softening temperature
-- 150 °C ASTM 1525 10
-- 148 °C ISO 306/A50
-- 143 °C ISO 306/B50
Linear coefficient of thermal expansion - Flow (44 to 100 ° C) 6.0E-5 to 8.0E-5 cm/cm/° C ASTM 696
Thermal conductivity 0.20 W/m/K ASTM C177
Test method for unit system of rated electrical performance values
Volume resistivity 3.0E+16 ohms · cm ASTM 257
Dielectric strength (1.60 mm) 30 kV/mm ASTM 149
Dielectric constant ASTM 150
60 Hz 2.95 ASTM 150
1 MHz 2.90 ASTM 150
Dissipation factor ASTM 150
60 Hz 4.0E-4 ASTM 150
1 MHz 9.0E-3 ASTM 150
Arc resistance 11 110 sec ASTM 495
Test method for flammability rating unit system
UL flame retardant rating (1.50 mm) V-2 UL 94
Test method for optical performance rating unit system
Refractive index 1.585 ASTM 542
Transmittance (76200 μ m) 88.0% ASTM 1003
Haze (81300 μ m)<; 0.80 % ASTM 1003
Injection rated value unit system
Drying temperature 120 ° C
Drying time 4.0 hours
The temperature at the back of the barrel is 230 to 300 ° C
The temperature in the middle of the barrel is 250 to 320 ° C
The temperature at the front of the barrel ranges from 250 to 310 ° C
Mold temperature 70.0 to 120 ° C
AfterSalesService :
Key words:- Automotive Parts PC