Description :

　　Impact resistant PC 500R SABIC basic fiberglass 10% flame retardant 5VA high rigidity

　　LEXAN? 500R resin polycarbonate 10% glass fiber reinforced material

　　LEXAN? Property Table of 500R Resin

　　Basic Information

　　Filler/reinforcement material glass fiber reinforcement material, 10% filler by weight

　　Additive demolding

　　Characteristic rigidity, high impact resistance, and good flame retardancy

　　Processing method: Injection molding

　　Physical performance rating unit testing method

　　Specific gravity ASTM 92

　　-- 1.27 g/cm3 ASTM 792

　　-- 1.25 g/cm3 ASTM 792

　　Specific volume 0.802 cm3/g ASTM 792

　　Test method for flammability rating unit system

　　Radiant Panel Listing (UL) YES

　　Physical performance rating unit testing method

　　Melt flow rate (300 ° C/1.2 kg) 7.5 g/10 min ASTM 1238

　　Shrinkage rate - Flow (3.20 mm) 0.20 to 0.40% Internal method

　　Water absorption rate ASTM 570

　　24 hr 0.12 % ASTM 570

　　Balance, 23 ° C 0.31% ASTM 570

　　Outdoor Applicability f2 UL 746C

　　Test method for hardness rating unit system

　　Rockwell hardness ASTM 785

　　M-grade 85 ASTM 785

　　R-grade 124 ASTM 785

　　Mechanical performance rating unit testing method

　　Tensile strength 1 ASTM 638

　　Yield 66.2 MPa ASTM 638

　　Fracture 55.2 MPa ASTM 638

　　Elongation rate 2 ASTM 638

　　Yield 8.0% ASTM 638

　　Fracture 15% ASTM 638

　　Bending modulus 3 (50.0 mm span) 3450 MPa ASTM 790

　　Bending strength 4 (yield, 50.0 mm span) 103 MPa ASTM 790

　　Taber Wear Resistance (1000 Cycles, 1000 g, CS-17 Wheel) 11.0 mg ASTM 1044

　　Test method for impact performance rating unit system

　　Suspended wall beam notch impact strength (23 ° C) 110 J/m ASTM 256

　　Notchless cantilever beam impact (23 ° C) 2100 J/m ASTM 4812

　　Drop hammer impact (23 ° C) 102 J ASTM

　　Tensile impact strength 5 158 kJ/m2 ASTM 1822