- Product Description
-
Description :
PC 6485 Shanghai Covestro
MVR (300 ° C/1.2 kg) 9.0cm3/10 minutes; Not flammable; UL 94V-0/1.5mm and 5VA/3.0mm; Medium viscosity; Easy to release; Injection molding - melt temperature 280-320 ° C;
Large and small household appliances
5VA; containing release agent; V-0; Flame retardant; V-1;
6485 Physical Property Table
Basic Information
Yellow card number E41613-233150
E41613-233151
Additive flame retardancy
Good demolding performance
Medium viscosity
flame retardancy
RoHS Compliance RoHS Compliance
Opaque appearance
Available colors
Processing method: Injection molding
Multi point data Creep Module vs. Time (ISO 11403-1)
Isochronous Stress vs. Strain (ISO 11403-1)
Isothermal Stress vs. Strain (ISO 11403-1)
Secant Modulus vs. Strain (ISO 11403-1)
Shear Modulus vs. Temperature (ISO 11403-1)
Specific Volume vs Temperature (ISO 11403-2)
Viscosity vs. Shear Rate (ISO 11403-2)
Physical performance rating unit testing method
Density (23 ° C) 1.20 g/cm3 ISO 1183
Apparent density 1 0.64 g/cm3 ISO 60
Melt flow rate (melt flow rate) (300 ° C/1.2 kg) 10 g/10 min ISO 1133
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 9.00 cm3/10 min ISO 1133
shrinkage rate
Vertical flow direction 0.60 to 0.80% ISO 2577
Flow direction 0.60 to 0.80% ISO 2577
Vertical flow direction: 2.00 mm 2 0.70% ISO 294-4
Flow direction: 2.00 mm 3 0.65% ISO 294-4
Water absorption rate ISO 62
Saturation, 23 ° C 0.30% ISO 62
Balance, 23 ° C, 50% RH 0.12% ISO 62
Test method for hardness rating unit system
Ball compression hardness 115 MPa ISO 2039-1
Mechanical performance rating unit testing method
Tensile modulus (23 ° C) 2400 MPa ISO 527-2/1
Tensile stress ISO 527-2/50
Yield, 23 ° C 66.0 MPa ISO 527-2/50
Fracture, 23 ° C 65.0 MPa ISO 527-2/50
Tensile strain ISO 527-2/50
Yield, 23 ° C 6.1% ISO 527-2/50
Fracture, 23 ° C 120% ISO 527-2/50
Nominal tensile fracture strain (23 ° C)>; 50 % ISO 527-2/50
Tensile creep modulus ISO 899-1
1 hr 2200 MPa ISO 899-1
1000 hr 1900 MPa ISO 899-1
Bending modulus 4 (23 ° C) 2400 MPa ISO 178
Bending stress 5 ISO 178
3.5% strain, 23 ° C 74.0 MPa ISO 178
23°C 98.0 MPa ISO 178
Flexural Strain at Flexural Strength (23°C) 6 7.1 % ISO 178
Test method for flammability rating unit system
Application of Flame from Small Burner - Method K and F (2.00 mm) K1, F1 DIN 53438-1, -3
Burning Rate - US-FMVSS (> 1.00 mm) passed ISO 3795
Flash Ignition Temperature 460 °C ASTM 1929
Glow Wire Test EDF HN60 E.02
1.50 mm 750 °C EDF HN60 E.02
3.00 mm 750 °C EDF HN60 E.02
Needle Flame Test IEC 60695-11-5
Method F : 1.50 mm 2.0 min IEC 60695-11-5
Method F : 2.00 mm 2.0 min IEC 60695-11-5
Method F : 3.00 mm 2.0 min IEC 60695-11-5
Method K : 1.50 mm 2.0 min IEC 60695-11-5
Method K : 2.00 mm 2.0 min IEC 60695-11-5
Method K : 3.00 mm 2.0 min IEC 60695-11-5
Self Ignition Temperature 540 °C ASTM 192