- Product Description
-
Description :
PC 3103 Shanghai Covestro
Specification level: Injection molding
Product Usage: Used for general industrial products, does not contain release agents.
Note: Characteristics: Medium to high molecular weight, injection or extrusion molding, good physical and mechanical properties.
3103 Physical Property Table
Basic performance rating unit testing method
Density 1200 KG/m ISO 1183
Melt flow rate (mass) (300 ℃. 1.2kg) 6.5 g/10min ISO 1133
Thermal absorption (relative temperature of 23 ℃/50 ℃) 0.12% ISO 62
Melt flow rate (volume) (300 ℃. 1.2kg) 6 cm/mm ISO 1133
Water absorption (saturation value 23 ℃, saturation) 0.3% ISO 62
Volume resistivity 10 Ω. m IEC 60093
Physical performance rating unit testing method
Transmittance (transparent material) DIN 5036-1
(4mm) 87 %
(3mm) 88 %
Haze (transparent material) (3mm) ＜ 0.8% ISO 14782
Transmittance (transparent material) (2mm) 89% DIN 5036-1
Refractive index 1.587 ISO 489
Transmittance (transparent material) (1mm) 89% DIN 5036-1
Mechanical performance rating unit testing method
Charpy impact strength (-30 ℃) N KJ/m ISO 179-1eU
Tensile modulus (1mm/min) 2400 MPa ISO 527
Yield stress (50mm/min) 65 MPa ISO 527
IZOD notch impact strength (23 ℃) 90 KJ/m ISO 180-4A
Charpy impact strength (23 ℃) N KJ/m ISO 179-1eU
Tensile creep modulus (1000h) 1900 MPa ISO 899-1
Nominal tensile strain at break (50mm/min)>50% ISO 527
IZOD notch impact strength (-30 ℃) 12 KJ/m ISO 180-4A
Tensile creep modulus (1h) 2200 MPa ISO 899-1
Yield strain (50mm/min) 6.5% ISO 527
Unit testing method for rated electrical performance values
Surface resistivity 10 Ω IEC 60093
Anti arc track performance (solution A/SolutionA) 275 grade/Rating IEC 60112
Penetration energy (-30 ℃/2mm) 70 J ISO 6603-2
Loss factor
(1MHz) 90 10-4 IEC 60093
(100Hz) 5 10-4 IEC 60250
Relative dielectric constant (100Hz) 3.1 IEC 60250
Penetration energy (23 ℃/2mm) 65 J ISO 6603-2
Penetration ISO 6603-2
(23℃/2mm) 5600 N
(-30℃/2mm) 6600 N
Relative dielectric constant (1MHz) 3.0 IEC 60250
Dielectric strength (1mm) 32 kV/mm IEC 60243-1
Unit testing method for rated values of processing performance
Forming shrinkage rate ISO 1133
0.6-0.8 %
0.6-0.8 %
Unit testing method for thermal performance rating
Thermal expansion coefficient (23-55 ℃) 0.6 10-4/℃ ISO 11359-2
Thermal change temperature (1.80MPa) 127 ℃ ISO 75-2
Glow metal wire test temperature (1.0mm) 850 ℃ IEC 60695-2-12
Vicat softening temperature (50N. 50 ℃/h) 146 ℃ ISO 306
Glow metal wire test temperature (1.5mm) 850 ℃ IEC 60695-2-12
Burnability V-2/0.81 (HB/1.5) (HB/3.0) Category/Class UL 94 (ISO 1210) (ISO 10351)
Thermal change temperature (0.45MPa) 139 ℃ ISO 75-2
Glow metal wire test temperature (3.0mm) 900 ℃ IEC 60695-2-12
Melt temperature 300 ℃ ISO 294
Glass transition temperature (10 ℃/min) 148 ℃ ISO 11357-2
Mold temperature 80 ℃ ISO 294
Glow metal wire test temperature (2.0mm) 850 ℃ IEC 60695-2-12
Other performance rating unit testing methods
Injection speed 200 mm/s ISO 294
Oxygen index (Method A/Procedure A) 28% IEC 4589-2
Viscosity coefficient 64 cm/g ISO 1628-4