General PC 3105 Shanghai Kesichuang High Viscosity
Category:
Rubber and plastic/engineering plastic/PC
Model:
Brand:
Shanghai Bayer
Retail Price
22.80USD
重量
kg
- Product Description
-
Description :
PC 3105 Shanghai Covestro
MVR (300 ° C/1.2 kg) 6.0cm3/10 minutes; General purpose; High viscosity is easy to release; Injection molding - melt temperature 280-320 ° C; available in transparent, semi transparent, and opaque colors
3105 Physical Property Table
Basic Information
Yellow card number E41613-233143
General characteristics
Good demolding performance
Viscosity, high
Universal use
RoHS Compliance RoHS Compliance
Appearance semi transparent
opaque
Available colors
Clear/Transparent
Processing method: Injection molding
Multi point data Creep Module vs. Time (ISO 11403-1)
Isochronous Stress vs. Strain (ISO 11403-1)
Isothermal Stress vs. Strain (ISO 11403-1)
Secant Modulus vs. Strain (ISO 11403-1)
Shear Modulus vs. Temperature (ISO 11403-1)
Specific Volume vs Temperature (ISO 11403-2)
Viscosity vs. Shear Rate (ISO 11403-2)
Physical performance rating unit testing method
Density (23 ° C) 1.20 g/cm3 ISO 1183
Apparent density 1 0.66 g/cm3 ISO 60
Melting rate (melt flow rate) (300 ° C/1.2 kg) 6.5 g/10 min ISO 1133
Dissolved Volume Flow Rate (MVR) (300 ° C/1.2 kg) 6.00 cm3/10 min ISO 1133
shrinkage rate
Vertical flow direction 0.60 to 0.80% ISO 2577
Flow direction 0.60 to 0.80% ISO 2577
Vertical flow direction: 2.00 mm 2 0.75% ISO 294-4
Flow direction: 2.00 mm 3 0.70% ISO 294-4
Water absorption rate ISO 62
Saturation, 23 ° C 0.30% ISO 62
Balance, 23 ° C, 50% RH 0.12% ISO 62
Test method for hardness rating unit system
Ball compression hardness 113 MPa ISO 2039-1
Mechanical performance rating unit testing method
Tensile modulus (23 ° C) 2400 MPa ISO 527-2/1
Tensile stress ISO 527-2/50
Yield, 23 ° C 66.0 MPa ISO 527-2/50
Fracture, 23 ° C 70.0 MPa ISO 527-2/50
Tensile strain ISO 527-2/50
Yield, 23 ° C 6.2% ISO 527-2/50
Fracture, 23 ° C 130% ISO 527-2/50
Nominal tensile fracture strain (23 ° C)>; 50 % ISO 527-2/50
Tensile creep modulus ISO 899-1
1 hr 2200 MPa ISO 899-1
1000 hr 1900 MPa ISO 899-1
Bending modulus 4 (23 ° C) 2400 MPa ISO 178
Bending stress 5 ISO 178
3.5% strain, 23 ° C 73.0 MPa ISO 178
23°C 97.0 MPa ISO 178
Flexural Strain at Flexural Strength (23°C) 6 7.1 % ISO 178
Test Method for Film Rating Unit System
Gas Permeation ISO 2556
Carbon Dioxide : 23°C, 25.4 μm 16900 cm3/m2/bar/24 hr ISO 2556
Carbon Dioxide : 23°C, 100.0 μm 3800 cm3/m2/bar/24 hr ISO 2556
Nitrogen : 23°C, 25.4 μm 510 cm3/m2/bar/24 hr ISO 2556
Nitrogen : 23°C, 100.0 μm 120 cm3/m2/bar/24 hr ISO 2556
Oxygen : 23°C, 25.4 μm 2760 cm3/m2/bar/24 hr ISO 2556
Oxygen : 23°C, 100.0 μm 650 cm3/m2/bar/24 hr ISO 2556
Test method for flammability rating unit system
Application of Flame from Small Burner - Method K and F (2.00 mm) K1, F1 DIN 53438-1, -3
Burning Rate - US-FMVSS (> 1.00 mm) passed ISO 3795
Flash Ignition Temperature 480 °C ASTM 1929
Glow Wire Test EDF HN60 E.02
1.50 mm 850 °C E