Industrial application of high refractive index COC Japanese Mitsui APL6011T
Category:
Rubber and plastic/engineering plastic/COC
Model:
Brand:
Mitsui Chemicals, Japan
Retail Price
65.00USD
重量
kg
- Product Description
-
Description :
Industrial application of high refractive index COC Japanese Mitsui APL6011T
COC/COP is a high-performance optical new material widely used in high-end pharmaceutical packaging materials, medical optical components, lenses, screens, and other optical fields. With the continuous expansion of mobile screen and lens applications, the COC/COP market has a vast space, and it is expected that the COC/COP market space may exceed 10 billion yuan by next year.
For a long time, China's COC/COP market has been mainly monopolized by foreign giants, and the required products are basically dependent on imports. In recent years, with the continuous increase in research and development efforts and the improvement of independent research and development capabilities of COC/COP in China, some Chinese enterprises have already possessed the potential for industrialization of COC/COP. Overall, the COC/COP market has a high level of attention, and China's COC/COP new materials field is already on the road. There is a large space for domestic substitution in the future, and the future is promising.
APEL APL6011T Physical Properties Table
Basic Information
Usage: Industrial Applications
Formal particle
Physical performance rating unit testing method
Specific gravity 1.03 g/cm3 ASTM 792
Melt flow rate (260 ° C/2.16 kg) 26 g/10 min ASTM 1238
Shrinkage rate - Flow 0.60% ASTM 955
Mechanical performance rating unit testing method
Tensile strength (yield) 60.0 MPa ASTM 638
Elongation (at break) 3.0% ASTM638
Bending modulus 2700 MPa ASTM 790
Bending strength 110 MPa ASTM 790
Test Method for Film Rating Unit System
Water vapor permeability 0.090 g · mm/m2/atm/24 hr ASTM F1249
Test method for impact performance rating unit system
Suspended wall beam notch impact strength 25 J/m ASTM256
Test method for thermal performance rating unit system
Hot deformation temperature under load (1.8 MPa, unannealed) 95.0 ° C ASTM 648
Glass transition temperature 105 ° C DSC
Test method for optical performance rating unit system
Refractive index 1.540 ASTM 542
Transmittance 90.0% ASTM 1003
Haze 3.0% ASTM 1003
AfterSalesService :
Key words:- High refractive index COC