Flame retardant PPE 220Z, Asahi Kasei PPO, heat-resistant

Description :

　　1、 Product Introduction

　　Polyoxyxylene is one of the inexpensive high-temperature resistant plastics, but it is difficult to manufacture and its impact and heat resistance will decrease over time. Mixing polyoxymethylene and polystyrene can improve this drawback. In the 1960s, adjusted polyethylene glycol was introduced under the trade name Noryl. The commonly used material in the market is modified polyphenylene oxide (MPPO), also known as MPPE (Modified Polyphenylene Ether).

　　Performance: Flame retardant

　　Usage: Automotive field

　　2、 Physical property table

　　220Z Modified Polyphenylene Ether Property Table

　　Physical performance rating (metric) rating (imperial) testing method

　　Specific gravity 1.08 g/cc 1.08 g/cc 23 ° C; ASTM 792

　　Moisture absorption 0.100% 0.100% 23 ° C, 50% RH 24 hours; ASTM 570

　　Linear forming shrinkage rate 0.0050-0.0070 cm/cm 0.0050-0.0070 in/in ASTM 955

　　Mechanical performance rating (metric) rating (imperial) testing method

　　Tensile strength (yield) 43.0 MPa 6240 psi 23 ° C, 50% RH; ASTM 638

　　Elongation (fracture) 50% 50% 23 ° C, 50% RH; ASTM 638

　　Bending strength 69.0 MPa 10000 psi 23 ° C, 50% RH; ASTM 790

　　Bending modulus 2.40 GPa 348 ksi at 23 ° C, 50% RH; ASTM 790

　　Suspended wall beam notch impact strength 1.47 J/ cm@Thickness 6.40 mm, Temperature 23.0 °C 2.75 ft-lb/ in@Thickness 0.252 in, Temperature 73.4 °F ASTM256

　　2.16 J/ cm@Thickness 3.20 mm, Temperature 23.0 °C 4.05 ft-lb/ in@Thickness 0.126 in, Temperature 73.4 °F ASTM 256

　　Electrical performance rating (metric) rating (imperial) testing method

　　Volume resistivity 1.00e+16 ohm cm 1.00e+16 ohm cm 50% RH; ASTM 257

　　Surface resistance 1.00e+16 ohm 1.00e+16 ohm 50% RH; ASTM 257

　　dielectric constant 2.9@Frequency 1e+6 Hz 2.9@Frequency 1e+6 Hz 3.0 mm 5VA; ASTM 150

　　2.9@Frequency 1e+6 Hz 2.9@Frequency 1e+6 Hz 50% RH; ASTM 150

　　Dielectric strength 29.0 kV/ mm@Thickness 2.00 mm 737 kV/ in@Thickness 0.0787 in Short time; ASTM 149

　　Dissipation factor 0.0030@Frequency 60 Hz 0.0030@Frequency 60 Hz 50% RH; ASTM 150

　　0.0040@Frequency 1e+6 Hz 0.0040@Frequency 1e+6 Hz 50% RH; ASTM 150

　　Arc resistance 80 sec 80 sec Tungsten; ASTM 495

　　Thermal performance rating (metric) rating (imperial) testing method

　　Linear coefficient of thermal expansion 80.0 μ m/m - ° C @ Temperature -30.0-60.0 ° C 44.4 μ in/in - ° F @ Temperature -22.0-140 ° F ASTM 696

　　Hot deformation temperature under load (1.8 MPa) 90.0 ° C 194 ° F ASTM 648

　　Flammability (UL94) V-0@Thickness 1.60 mm V-0@Thickness 0.0630 in

　　V-0@Thickness 3.20 mm V-0@Thickness 0.126 in

　　Processing performance rating (metric) rating (imperial) testing method

　　Processing temperature 220-270 ° C 428-518 ° F Resin Temperature

　　Mold temperature: 40.0-70.0 ° C, 104-158 ° F

　　Drying Temperature 80.0-90.0 ° C 176-194 ° F Pre drying Temperature

　　Drying time 2-4 hours 2-4 hours

　　3、 Product shooting

　　4、 Buyer Notice

　　1. Quality assuranceOur products are all original factory packaged, with affordable prices for first tier sources.

　　2. SafetyDue to love, purchasing cannot be done online. Customers can do it on Alibaba. Safe and reassuring. (Our company's Alibaba 12 Year Integrity Certification)

　　3. Fast deliveryIf there is stock available, it can be shipped on the same day. The bulk order will be shipped within 3 days, and specific details can be agreed upon.

　　4. Formal invoice13% value-added tax invoice can be issued.

　　5. Material certificationProvide original factory property table, SGS certification, yellow card UL, ROHS report, MSDS, etc.

AfterSalesService :

• Flame retardant PPE