Flame retardant PPO 1951J Japan Asahi Kasei PPE high flow

Description :

　　1、 Product Introduction

　　Polyoxyxylene is one of the inexpensive high-temperature resistant plastics, but it is difficult to manufacture and its impact and heat resistance will decrease over time. Mixing polyoxymethylene and polystyrene can improve this drawback. In the 1960s, adjusted polyethylene glycol was introduced under the trade name Noryl. The commonly used material in the market is modified polyphenylene oxide (MPPO), also known as MPPE (Modified Polyphenylene Ether).

　　Performance: Flame retardant V-1, high flowability

　　Usage: Automotive parts

　　2、 Physical property table

　　1951J Physical Property Table

　　Basic Information

　　Yellow card number E82268-250778

　　Additive flame retardancy

　　Good liquidity characteristics

　　flame retardancy

　　Processing method: Injection molding

　　Physical performance rating unit testing method

　　Density 1.11 g/cm3 ISO 1183

　　Shrinkage rate 1 (2.00 mm) 0.50 to 0.70% internal method

　　Water absorption rate (23 ° C, 24 hr) 0.10% ISO 62

　　Mechanical performance rating unit testing method

　　Tensile stress (yield, 23 ° C) 37.0 MPa ISO 527-2

　　Nominal tensile fracture strain (23 ° C) 30% ISO 527-2

　　Bending modulus (23 ° C) 2350 MPa ISO 178

　　Bending stress (23 ° C) 66.0 MPa ISO 178

　　Test method for impact performance rating unit system

　　Simply supported beam notch impact strength 2 (23 ° C) 12 kJ/m2 ISO 179

　　Test method for thermal performance rating unit system

　　Thermal deformation temperature under load

　　1.8 MPa, Unanealed 76.0 ° C ASTM 648

　　1.8 MPa, Unanealed 70.0 ° C ISO 75-2/A

　　Linear coefficient of thermal expansion - Flow (-30 to 65 ° C) 8.0E-5 cm/cm/° C ISO 11359-2

　　Test method for unit system of rated electrical performance values

　　Surface resistivity 1.0E+16 ohms IEC 60093

　　Volume resistivity (23 ° C) 1.0E+16 ohms · cm IEC 60093

　　Dielectric strength 3 (2.00 mm) 29 kV/mm IEC 60243-1

　　Dielectric constant IEC 60250

　　100 Hz 2.90 IEC 60250

　　1 MHz 2.90 IEC 60250

　　Dissipation factor IEC 60250

　　100 Hz 3.0E-3 IEC 60250

　　1 MHz 4.0E-3 IEC 60250

　　Test method for flammability rating unit system

　　UL flame retardant rating (2.00 mm) V-1 5VB UL 94

　　Injection rated value unit system

　　Drying temperature 70.0 to 80.0 ° C

　　Drying time 2.0 to 4.0 hours

　　Processing (melt) temperature 220 to 280 ° C

　　Mold temperature 40.0 to 70.0 ° C

　　3、 Product shooting

　　4、 Buyer Notice

　　1. Quality assuranceOur products are all original factory packaged, with affordable prices for first tier sources.

　　2. SafetyDue to love, purchasing cannot be done online. Customers can do it on Alibaba. Safe and reassuring. (Our company's Alibaba 12 Year Integrity Certification)

　　3. Fast deliveryIf there is stock available, it can be shipped on the same day. The bulk order will be shipped within 3 days, and specific details can be agreed upon.

　　4. Formal invoice13% value-added tax invoice can be issued.

　　5. Material certificationProvide original factory property table, SGS certification, yellow card UL, ROHS report, MSDS, etc.

AfterSalesService :

• Flame retardant PPO