High rigidity PES E2010C6 from BASF Germany, with high mechanical strength and dimensional stability, replacing PEEK

Description :

　　1、 Product Introduction

　　Polyether sulfone resin, a chemical raw material, is a transparent amber colored amorphous resin with excellent heat resistance, dimensional stability, and good chemical resistance. In addition, PES exhibits excellent reliability against rapid temperature changes and has good reliability for long-term use at high temperatures. The excellent formability and properties of PES make it widely used.

　　PEEK can maintain good electrical insulation in harsh environments such as high temperature, high pressure, and high humidity, and has characteristics such as being not easily deformed over a wide temperature range. Therefore, it is gradually being used as an ideal electrical insulation material in the field of electronics and electrical appliances.

　　Peek polymer material is used to make the outer shell of aluminum electrolytic containers, meeting the requirements of lead-free soldering technology in the electronics industry. The wafer cartridge made of PEEK material can control the dissipation of static charges, protect the wafer from damage, and reduce and prevent static accumulation to protect the wafer from pollution caused by electrostatic attraction.

　　2、 Physical property table

　　E 2010 C6 30% Carbon Filled Physical Properties Table

　　Physical performance rating (metric) rating (imperial) testing method

　　Bulk density 0.700-0.800 g/cc 0.0253-0.0289 lb/m3

　　Density 1.47 g/cc 0.0531 lb/in3 ISO 1183

　　Water absorption rate<=1.7%<; = 1.7 % Equilibrium; ISO 62

　　Balanced moisture absorption 0.60% 0.60% 23 ° C; 50% RH; ISO 62

　　Viscosity measurement 56 56 [cm³/g]; ISO 1628

　　Linear molding shrinkage rate, Flow 0.0015 cm/cm 0.0015 in/in ISO 294

　　Linear molding shrinkage rate, transverse 0.0035 cm/cm 0.0035 in/in ISO 294

　　Melt flow rate>=22.05 g/10 min@Load 10.0 kg, Temperature 360 °C > = 22.05 g/10 min@Load 22.0 lb, Temperature 680 °F ISO 1133

　　>= 45 g/10 min@Load 10.0 kg, Temperature 400 °C > = 45 g/10 min@Load 22.0 lb, Temperature 752 °F

　　Mechanical performance rating (metric) rating (imperial) testing method

　　Ball pressure hardness 227 MPa@Load 36.5 kg, Time 30.0 sec 32900 psi@Load 80.5 lb, Time 0.00833 hour ISO 2039-1

　　Tensile strength (fracture) 185 MPa 26800 psi 5 mm/min; ISO 527-2

　　Tensile strength (yield) 185 MPa 26800 psi 50 mm/min; ISO 527-2

　　Elongation (fracture) 1.5% 1.5% 5mm/min; ISO 527-2

　　Yield elongation 1.5% 1.5% 50 mm/min; ISO 527-2

　　3、 Product shooting

　　4、 Buyer Notice

　　1. Quality assurance. Our products are all original factory packaged, sourced from first tier sources, and priced affordably.

　　2. Safety. Public accounts are safe and reliable. (Our company's Alibaba 12 Year Integrity Certification)

　　3. Fast delivery. If the goods are available, they can be shipped on the same day. The bulk order will be shipped within 3 days, and specific details can be agreed upon.

　　4. Formal invoice. 13% value-added tax invoice can be issued.

　　5. Material certification. Provide original factory property tables, SGS certification, yellow card UL, ROHS reports, MSDS, and more.

　　6. Sample testing. We can provide sample testing for customers to improve the success rate of trial production.

　　Temperature dependence of modulus: Its modulus remains almost unchanged from -100 ℃ to 200 ℃, especially better than any thermoplastic resin above 100 ℃.

AfterSalesService :