High temperature and wear-resistant PEEK 450GL30, Japanese Teijin Food Medical Grade
VICTREX® PEEK 450GL30 polyetheretherketone
30% glass fiber reinforced material
VICTREX® PEEK 450GL30 Physical Properties Table
Basic Information
Filler/reinforcement material glass fiber reinforcement material, 30% filler by weight
Characteristics: Semi crystalline, low friction coefficient, high strength, good disinfection, good chemical resistance, compliance with food contact
Non specific food applications, medical/nursing supplies
Institutional rating FDA food contact, not rated MIL P-46183
Appearance beige, natural color
Form particles
High performance polymers are a new type of high-performance polymer material developed in the late 1960s. From polyimide, which was first introduced in 1960, to polyetheretherketone (PEEK), which was introduced in the early 1980s, major companies in Europe and America have conducted extensive research and development on this type of high-performance polymer. Although dozens of varieties have been developed, less than 10 of them have actual application value and industrialization. They are at the forefront of engineering plastics in terms of performance and commercial value.
Processing method: extrusion injection molding
Physical performance rating unit testing method
Density 1.51 g/cm3 ISO 1183
Spiral Flow 1 Internal Methods
--2 8.50 cm internal method
--3 41.0 cm internal method
shrinkage rate
Vertical flow direction: 190 ° C 4 0.90%
Flow direction: 190 ° C 5 0.30% ISO 294-4
Water absorption rate ISO 62
23°C, 24 hr, 3.20 mm 0.040 % ISO 62
Balance, 23 ° C, 3.20 mm, 50% RH 0.30% ISO 62
Test method for hardness rating unit system
Shore hardness (Shore D, 23 ° C) 88 ISO 868
Mechanical performance rating unit testing method
Tensile modulus (23 ° C) 11800 MPa ISO 527-2
Tensile stress ISO 527-2
Fracture, 23 ° C 180 MPa ISO 527-2
Fracture, 125 ° C 115 MPa ISO 527-2
Fracture, 175 ° C 60.0 MPa ISO 527-2
Fracture, 275 ° C 35.0 MPa ISO 527-2
Tensile strain (fracture, 23 ° C) 2.7% ISO 527-2
Bending modulus (23 ° C) 11300 MPa ISO 178
Bending stress ISO 178
23°C 270 MPa ISO 178
125°C 190 MPa ISO 178
175°C 80.0 MPa ISO 178
275°C 50.0 MPa ISO 178
Compressive stress ISO 604
23°C 250 MPa ISO 604
120°C 160 MPa ISO 604
200°C 55.0 MPa ISO 604
Test method for impact performance rating unit system
Simply supported beam notch impact strength (23 ° C) 8.0 kJ/m2 ISO 179/1eA
Simply supported beam without notch impact strength (23 ° C) 55 kJ/m2 ISO 179/1U
Suspended wall beam notch impact strength (23 ° C) 10 kJ/m2 ISO 180/A
Unscented Izod impact strength (23 ° C) 60 kJ/m2 ISO 180