Flame retardant PES J1000 SABIC Basic Innovative Plastic

Description :

　　1、 Product Introduction

　　Polyether sulfone resin, a chemical raw material, is a transparent amber colored amorphous resin with excellent heat resistance, dimensional stability, and good chemical resistance. In addition, PES exhibits excellent reliability against rapid temperature changes and has good reliability for long-term use at high temperatures. The excellent formability and properties of PES make it widely used.

　　Can maintain stable high mechanical properties in high temperature environments. For example, the tensile strength can still maintain 50% after 5 years of use at 200 ℃.

　　flame retardant

　　2、 Physical property table

　　J1000 compound property table

　　RoHS Compliance RoHS Compliance

　　Processing method: Injection molding

　　Physical performance rating unit testing method

　　Density 1.37 g/cm3 ISO 1183

　　Shrinkage rate - Flow 1.0% internal method

　　Water absorption rate (23 ° C, 24 hr) 0.60% ISO 62

　　Mechanical performance rating unit testing method

　　Tensile modulus 2700 MPa ISO 527-2/1

　　Tensile stress ISO 527-2/50

　　Yield 91.0 MPa ISO 527-2/50

　　Fracture 67.0 MPa ISO 527-2/50

　　Tensile strain (yield) 6.8% ISO 527-2/50

　　Bending modulus 1 2600 MPa ISO 178

　　Bending stress 128 MPa ISO 178

　　Test method for impact performance rating unit system

　　Suspended wall beam notch impact strength 2 (23 ° C) 7.0 kJ/m2 ISO 180/1A

　　Unscented Izod Impact Strength 3 (23 ° C) No Fracture ISO 180/1U

　　Test method for thermal performance rating unit system

　　Hot deformation temperature 4

　　0.45 MPa, Unanealed, 64.0 mm span, 216 ° C ISO 75-2/Bf

　　1.8 MPa, Unanealed, 64.0 mm span 201 ° C ISO 75-2/Af

　　Linear coefficient of thermal expansion ISO 11359-2

　　Flow: 23 to 60 ° C 5.9E-5 cm/cm/° C ISO 11359-2

　　Horizontal: 23 to 60 ° C 5.9E-5 cm/cm/° C ISO 11359-2

　　Flammability rating test method

　　UL flame retardant rating (0.500 mm) V-0 UL 94

　　Injection rated value unit system

　　Drying temperature 121 to 149 ° C

　　Drying time 4.0 hours

　　Suggested moisture content 0.050%

　　The temperature at the rear of the barrel is 343 to 354 ° C

　　The temperature in the middle of the barrel is 360 to 371 ° C

　　The temperature at the front of the barrel is 371 to 382 ° C

　　Processing (melt) temperature 354 to 371 ° C

　　Mold temperature 138 to 149 ° C

　　Back pressure ranging from 0.344 to 0.689 MPa

　　Screw speed 60 to 100 rpm

　　3、 Product shooting

　　4、 Buyer Notice

　　1. Guarantee. Our products are all original factory packaged, sourced from first tier sources, and priced affordably.

　　2. Safety. Public accounts are safe and reliable. (Our company's Alibaba 12 Year Integrity Certification)

　　3. Fast delivery. If the goods are available, they can be shipped on the same day. The bulk order will be shipped within 3 days, and specific details can be agreed upon.

　　4. Formal invoice. 13% value-added tax invoice can be issued.

　　5. Material certification. Provide original factory property tables, SGS certification, yellow card UL, ROHS reports, MSDS, and more.

　　6. Sample testing. We can provide sample testing for customers to improve the success rate of trial production.

　　Good creep resistance and outstanding dimensional stability. The impact strength without notches can reach 93kJ/mz, almost the same as PC, but the impact strength is greatly affected by the notch radius. As the notch radius decreases, the impact strength will rapidly decrease.

AfterSalesService :

• Flame retardant PES