High heat PEI based on American 1010 food contact grade
Category:
Rubber and plastic/engineering plastic/PEI
Model:
Brand:
US GE
Retail Price
52.00USD
重量
kg
- Product Description
-
Description :
PEI with high thermal conductivity, based on American 1010 food contact grade, has good mechanical strength
Chemical resistance, high temperature resistance, flame retardant, easy to flow, fire rating 5 V0
PEI Shaber Foundation 1010 UltEM? 1010 resin
polyetherimideIntroduction to PEI 1010：
ULTEM? 1010 resin is an amorphous transparent polyetherimine (PEI) plastic with enhanced fluidity and a glass transition temperature (Tg) of 217 ℃.
This inherent flame retardant resin has UL94 V0 and 5VA ratings.
For medical applications that require biocompatibility, we recommend UltEMTM HU1010 resin as an alternative.
Passed the US FDA and EU food contact testing.
UltEMTM 1010 resin is a non reinforced general-purpose resin with high heat resistance, strength, modulus, and high-temperature chemical resistance.
ULTEM? 1010 Resin Physical Properties Table
Basic Information feature
High strength, good fluidity, good chemical resistance, heat resistance, high universal amorphous flame retardancy
purpose General grade food contact grade
RoHS compliance
appearance Clear/Transparent
processing method injection molding
Physical properties rated value system of units test method
Density 1.27 g/cm3 ISO 1183
Dissolved Volume Flow Rate (MVR) ISO 1133
340°C/5.0 kg 13.0 cm3/10min ISO 1133
360°C/5.0 kg 25.0 cm3/10min ISO 1133
Shrinkage rate - Flow rate of 0.50 to 0.70% Internal method
Water absorption rate ISO 62
Saturation, 23 ° C 1.3% ISO 62
Balance, 23 ° C, 50% RH 0.70% ISO 62
hardness rated value system of units test method
Ball indentation hardness (H 358/30) 140 MPa ISO 2039-1
Mechanical performance rating unit testing method
Tensile modulus 3200 MPa ISO 527-2/1
Tensile stress ISO 527-2/50
Yield 105 MPa ISO 527-2/50
Fracture at 85.0 MPa ISO 527-2/50
Tensile strain ISO 527-2/50
Yield 6.0% ISO 527-2/50
Fracture 60% ISO 527-2/50
Bending modulus 2 3300 MPa ISO 178
Bending stress 160 MPa ISO 178
Taber Wear Resistance (1000 Cycles, 1000 g, CS-17 Wheel) 10.0 mg Internal Method