Fiberglass reinforced PPO SE1GFN1-701 Sabah base black heat-resistant sports equipment

Description :

　　1、 Product Introduction

　　Polyoxyxylene is one of the inexpensive high-temperature resistant plastics, but it is difficult to manufacture and its impact and heat resistance will decrease over time. Mixing polyoxymethylene and polystyrene can improve this drawback. In the 1960s, adjusted polyethylene glycol was introduced under the trade name Noryl. The commonly used material in the market is modified polyphenylene oxide (MPPO), also known as MPPE (Modified Polyphenylene Ether).

　　Performance: Enhanced; Fiberglass reinforcement; Flame retardant; High mobility; high temperature resistance

　　Usage: Electronic communication plastic parts and accessories; Large and small household appliances; Automotive internal components; Sports equipment, water

　　2、 Physical property table

　　SE1GFN1-701 Physical Property Table

　　Basic performance rating unit testing method

　　Water absorption rate (24 hours) 0.07% ASTM -570

　　Physical performance rating unit testing method

　　Mold shrinkage rate (3.2mm) 3-5 10-3 ASTM -955

　　Enhance by 10%

　　Flame retardant 1.5 mm UL 94

　　Specific gravity 1.16 ASTM 792

　　Mechanical performance rating unit testing method

　　Tensile strength ASTM-

　　(3.2mm) 74 MPa

　　(3.2mm) 5 MPa

　　Bending modulus (6.4mm) 3996 MPa ASTM -790

　　Notch impact strength (-40 ° C) 69 J/M ASTM -256

　　Rockwell hardness 104 ASTM

　　Flame retardant V-1 UL 94

　　Notch impact strength (23 ° C) 96 J/M ASTM -256

　　Unit testing method for rated electrical performance values

　　Loss factor (1MHz) 0.0016 ASTM -150

　　Dielectric constant (1MHz) 3 ASTM -150

　　Volume resistivity 1.0 × 10 Ω. cm ASTM -257

　　Unit testing method for thermal performance rating

　　Vicat softening point 147 ° C ASTM -1525

　　UL long-term use temperature UL 746B

　　110 °C

　　105 °C

　　110 °C

　　Hot deformation temperature (1MPa) 131 ° C

　　 3、 Product shooting

AfterSalesService :

• Fiberglass reinforced PPO