- Product Description
-
Description :
High flow PEI 9085 basic innovative plastic American low smoke and low toxicity
PEI 9085 color codes include 9085-1100, 9085-WH8E187, 9085-8173, 9085-BK1D701, and so on. You can contact us for consultation.
ULTEM? 9085 Resin Physical Properties Table
Basic Information feature
Low smoke, low toxicity, high fluidity
institutional rating
FAR 25.853OSU 55/55
RoHS compliance
RoHS compliance
processing method
Profile extrusion molding injection molding
Physical properties rated value system of units test method
Specific gravity 1.34 g/cm3
Melt flow rate (295 ° C/6.6 kg) 8.9 g/10 min
Dissolved Volume Flow Rate (MVR) (360 ° C/5.0 kg) 65.5 cm3/10 min ISO 1133
Shrinkage rate - flow (3.20 mm) 0.50 to 0.70% internal method
Water absorption rate ISO 62
Saturation, 23 ° C 0.39% ISO 62
Balance, 23 ° C, 50% RH 0.17% ISO 62
thermal performance rated value system of units test method
Thermal deformation temperature under load
1.8 MPa, Unanealed, 3.20 mm, 153 ° C
1.8 MPa, Unanealed, 64.0 mm span 10 152 ° C ISO 75-2/Af
Vicat softening temperature 173 ° C ISO 306/B120
Linear coefficient of thermal expansion
Flow: -30 to 80 ° C 6.0E-5 cm/cm/° C
Horizontal: -30 to 80 ° C 6.0E-5 cm/cm/° C
Drying temperature 120 to 130 ° C
Drying time 4.0 to 6.0 hours
Moisture content 0.020%
Suggested injection volume of 40 to 60%
The temperature at the rear of the barrel is 315 to 340 ° C
The temperature in the middle of the barrel is 325 to 345 ° C
The temperature at the front of the barrel is 330 to 350 ° C
Spray nozzle temperature 330 to 350 ° C
Processing (melt) temperature 330 to 350 ° C
Mold temperature 120 to 150 ° C
Back pressure 0.300 to 0.700 MPa
Screw speed 40 to 70 rpm
Exhaust hole depth 0.025 to 0.076 mm
impact performance rated value system of units test method
Simply supported beam notch impact strength (23 ° C) 11 kJ/m2 ISO 179/2C
Impact strength of cantilever beam gap
23°C 120 J/m
23°C 9 13 kJ/m2 ISO 180/1A