Flame retardant PES E 2010 HC German BASF impact resistant high flow

Description :

　　1、 Product Introduction

　　Polyether sulfone resin, a chemical raw material, is a transparent amber colored amorphous resin with excellent heat resistance, dimensional stability, and good chemical resistance. In addition, PES exhibits excellent reliability against rapid temperature changes and has good reliability for long-term use at high temperatures. The excellent formability and properties of PES make it widely used.

　　2、 Physical property table

　　E 2010 HC PESU Physical Property Table

　　Physical performance rating (metric) rating (imperial) testing method

　　Bulk density 0.700-0.800 g/cc 0.0253-0.0289 lb/m3

　　Density 1.37 g/cc 0.0495 lb/in3 ISO 1183

　　Water absorption rate 2.2% 2.2% ISO 62

　　Balanced moisture absorption 0.80% 0.80% 23 ° C; 50% RH; ISO 62

　　Viscosity measurement 56 56 [cm³/g]; ISO 307

　　Linear molding shrinkage rate, Flow 0.0082 cm/cm 0.0082 in/in ISO 2577, 294-4

　　Linear forming shrinkage rate, transverse 0.0086 cm/cm 0.0086 in/in ISO 2577, 294-4

　　Melt flow rate 95.9 g/10 min@Load 10.0 kg, Temperature 360 °C 95.9 g/10 min@Load 22.0 lb, Temperature 680 °F ISO 1133

　　Mechanical performance rating (metric) rating (imperial) testing method

　　Ball pressure hardness 154 MPa@Load 36.5 kg, Time 30.0 sec 22300 psi@Load 80.5 lb, Time 0.00833 hour ISO 2039-1

　　Tensile strength (yield) 90.0 MPa 13100 psi 50mm/min; ISO 527-1/-2

　　Yield elongation 6.7% 6.7% 50mm/min; ISO 527-1/-2

　　Tensile modulus 2.70 GPa 392 ksi ISO 527-1/-2

　　Suspended wall beam notch impact strength 6.50 kJ/ m2@Temperature 23.0 °C 3.09 ft-lb/ in2@Temperature 73.4 °F ISO 180/A

　　7.00 kJ/ m2@Temperature -30.0 °C 3.33 ft-lb/ in2@Temperature -22.0 °F ISO 180/A

　　Impact strength of simply supported beam without notch NB@Temperature -30.0 °C NB@Temperature -22.0 °F ISO 179/1eU

　　NB@Temperature 23.0 °C NB@Temperature 73.4 °F ISO 179/1eU

　　The impact strength of the simply supported beam gap is 0.650 J/ cm2@Temperature 23.0 °C 3.09 ft-lb/ in2@Temperature 73.4 °F ISO 179/1eA

　　0.700 J/ cm2@Temperature -30.0 °C 3.33 ft-lb/ in2@Temperature -22.0 °F ISO 179/1eA

　　Tensile creep modulus (1000 hr) 2700 MPa@Strain <=0.500 % 392000 psi@Strain <=0.500 % ISO 899-1

　　Electrical performance rating (metric) rating (imperial) testing method

　　Volume resistivity>=1.00e+13 ohm cm>; = 1.00e+13 ohm-cm IEC 60093

　　dielectric constant 3.8@Frequency 1.00e+6 Hz 3.8@Frequency 1.00e+6 Hz ISO 60250

　　3.9@Frequency 100 Hz 3.9@Frequency 100 Hz ISO 60250

　　Dielectric strength 35.0 kV/mm 889 kV/in IEC 60243-1

　　Dissipation factor 0.0017@Frequency 100 Hz 0.0017@Frequency 100 Hz IEC 60250

　　0.014@Frequency 1.00e+6 Hz 0.014@Frequency 1.00e+6 Hz IEC 60250

　　Compared to the Leakage Traceability Index (CTI) 100 V 100 V Test Liquid A; IEC 60112

　　100 V 100 V Test Liquid B; IEC 60112

　　Thermal performance rating (metric) rating (imperial) testing method

　　Linear coefficient of thermal expansion - Flow 52.0 μ m/m - ° C @ Temperature 23.0-80.0 ° C 28.9 μ in/in - ° F @ Temperature 73.4-176 ° F ISO 75-1/-2

　　59.0 μm/m-°C@Temperature 180 °C 32.8 μin/in-°F@Temperature 356 °F DIN 53752

　　Working temperature, Air 180 ° C 356 ° F at 50% loss of tensile strength after 20000 hours

　　220 °C 428 °F

　　Hot deformation temperature under load (1.8 MPa) 205 ° C 40

　　3、 Product shooting

　　4、 Buyer Notice

　　1. Guarantee. Our products are all original factory packaged, sourced from first tier sources, and priced affordably.

　　2. Safety. Public accounts are safe and reliable. (Our company's Alibaba 12 Year Integrity Certification)

　　3. Fast delivery. If the goods are available, they can be shipped on the same day. The bulk order will be shipped within 3 days, and specific details can be agreed upon.

　　4. Formal invoice. 13% value-added tax invoice can be issued.

　　5. Material certification. Provide original factory property tables, SGS certification, yellow card UL, ROHS reports, MSDS, and more.

　　6. Sample testing. We can provide sample testing for customers to improve the success rate of trial production.

　　Impact resistance: It has the same impact resistance as polycarbonate. Unreinforced resin can be riveted, but for sharp PES products, the incision is more sensitive, so design attention should be paid.

AfterSalesService :

• Flame retardant PES