Chemical resistant PPO GTX914 Sabouraud based high-strength and wear-resistant electric tool
Category:
Rubber and plastic/engineering plastic/PPO
Model:
Brand:
Saudi Arabia Foundation
Retail Price
36.00USD
重量
kg
- Product Description
-
Description :
1、 Product Introduction
Polyoxyxylene is one of the inexpensive high-temperature resistant plastics, but it is difficult to manufacture and its impact and heat resistance will decrease over time. Mixing polyoxymethylene and polystyrene can improve this drawback. In the 1960s, adjusted polyethylene glycol was introduced under the trade name Noryl. The commonly used material in the market is modified polyphenylene oxide (MPPO), also known as MPPE (Modified Polyphenylene Ether).
Performance: Chemical resistance; High intensity; High temperature resistance; wear-resisting; high impact resistance
Purpose: In the field of electrical/electronic applications for power tools; Electronic display; External components of automobiles; Automotive internal components
2、 Physical property table
GTX914 Physical Properties Table
Basic performance rating unit testing method
Density 1.09 g/cm ISO 1183
Water absorption rate 3.50% DIN 53495
Physical performance rating unit testing method
Hardness (H358/30) 90 MPa ISO 2039/1
Mechanical performance rating unit testing method
Tensile strength ISO 527
(50mm/min, yield) 55 MPa
(50mm/min, fracture) 55 MPa
Tensile elongation ISO 527
(50mm/min, yield) 7.5%
(50mm/min, fracture) 60%
Tensile modulus (1mm/min) 2100 MPa ISO 527
Bending strength (2mm/min) 80 MPa ISO 178
Bending modulus (2mm/min) 2000 MPa ISO 178
Simply supported beam notch impact strength (23 ℃) 30 KJ/m ISO 179/2C
IZOD Impact Strength ISO 180/1A
(23 ℃ with gap) 30 KJ/m
(with a gap at -30 ℃) 15 KJ/m
Unit testing method for rated electrical performance values
Electrical strength 20.0KV/mm IEC 243
Electrical factors IEC 250
(50Hz) 0.0720
(1MHz) 0.0240
Unit testing method for rated values of processing performance
Mold shrinkage rate 1.5-1.9% ASTM 955
Unit testing method for thermal performance rating
Thermal conductivity coefficient 0.23 W/m ℃ DIN 52612
Linear thermal expansion coefficient 9E-5 1/℃ DIN 53752
Vicat hot deformation temperature ISO 306
(A/50) 245 ℃
(B/50) 190 ℃
(B/120) 195 ℃
Other performance rating unit testing methods
Oxygen index 21%
3、 Product shooting
AfterSalesService :
Key words:- Chemical resistant PPO