30% Fiberglass Reinforced PPO KR 2403 G6 BASF Germany Heat Resistant

Description :

　　1、 Product Introduction

　　Polyoxyxylene is one of the inexpensive high-temperature resistant plastics, but it is difficult to manufacture and its impact and heat resistance will decrease over time. Mixing polyoxymethylene and polystyrene can improve this drawback. In the 1960s, adjusted polyethylene glycol was introduced under the trade name Noryl. The commonly used material in the market is modified polyphenylene oxide (MPPO), also known as MPPE (Modified Polyphenylene Ether).

　　Performance: The universal grade glass fiber content is 30%, used for parts that require particularly good heat resistance and deformation resistance.

　　Usage: Used for parts that come into contact with hot water, pump casing, fan blades.

　　2、 Physical property table

　　KR 2403 G6 Polyphenylene Ether + Styrene-Butadiene Blend, 30% Glass Fiber Reinforced Physical Property Table

　　Physical performance rating (metric) rating (imperial) testing method

　　Density 1.26 g/cc 0.0455 lb/in3

　　Water absorption rate 0.30% 0.30%

　　Balanced moisture absorption 0.10% 0.10%

　　Linear molding shrinkage rate, Flow 0.0030 cm/cm 0.0030 in/in

　　High Load Melt Index 7.0 g/10 min@Load 21.6 kg, Temperature 250 °C 7.0 g/10 min@Load 47.6 lb, Temperature 482 °F

　　Mechanical performance rating (metric) rating (imperial) testing method

　　Ultimate tensile strength 110 MPa 16000 psi

　　Elongation (at break) 2.5% 2.5%

　　Tensile modulus 9.00 GPa 1310 ksi

　　Simply supported beam without notch impact strength 4.00 J/cm2 19.0 ft lb/in2

　　4.00 J/ cm2@Temperature -30.0 °C 19.0 ft-lb/ in2@Temperature -22.0 °F

　　The impact strength of the simply supported beam gap is 1.40 J/cm2 and 6.66 ft-lb/in2

　　1.40 J/ cm2@Temperature -30.0 °C 6.66 ft-lb/ in2@Temperature -22.0 °F

　　Tensile creep modulus (1 hr) 7100 MPa 1.03e+6 psi

　　Tensile creep modulus (1000 hr) 6100 MPa 885000 psi

　　Electrical performance rating (metric) rating (imperial) testing method

　　Electrical resistivity>=1.00e+15 ohm cm>; = 1.00e+15 ohm-cm

　　Surface resistance 1.00e+14 ohm 1.00e+14 ohm

　　dielectric constant 2.9@Frequency 100 Hz 2.9@Frequency 100 Hz

　　2.9@Frequency 1e+6 Hz 2.9@Frequency 1e+6 Hz

　　Dielectric strength 90.0 kV/mm 2290 kV/in

　　Dissipation factor 0.0010@Frequency 1e+6 Hz 0.0010@Frequency 1e+6 Hz

　　Compared to the Leakage Tracking Index (CTI) of 250 V 250 V

　　Thermal performance rating (metric) rating (imperial) testing method

　　Linear coefficient of thermal expansion - flow 35.0 μ m/m - ° C @ Temperature 20.0 ° C 19.4 μ in/in - ° F @ Temperature 68.0 ° F

　　Hot deformation temperature under load (0.46 MPa) 145 ° C 293 ° F

　　Hot deformation temperature under load (1.8 MPa) 141 ° C 286 ° F

　　Vicat softening temperature 145 ° C 293 ° F

　　Flammability (UL94) HB@Thickness 3.20 mm HB@Thickness 0.126 in

　　3、 Product shooting

　　4、 Buyer Notice

　　1. GuaranteeOur products are all original factory packaged, sourced from first tier sources at affordable prices.

　　2. SafetyDue to love, purchasing cannot be done online. Customers can do it on Alibaba. Safe and reassuring. (Our company's Alibaba 12 Year Integrity Certification)

　　3. Fast deliveryIf there is stock available, it can be shipped on the same day. The bulk order will be shipped within 3 days, and specific details can be agreed upon.

　　4. Formal invoice13% value-added tax invoice can be issued.

　　5. Material certificationProvide original factory property table, SGS certification, yellow card UL, ROHS report, MSDS, etc.

AfterSalesService :

• Fiberglass reinforced PPO