30% fiberglass reinforced LCP 6130LX, DuPont flame retardant V0 from the United States
Category:
Rubber and plastic/engineering plastic/LCP
Model:
Brand:
DuPont, USA
Retail Price
68.00USD
重量
kg
- Product Description
-
Description :
LCP 6130LX DuPont, USA
6130LX is a 30% glass fiber reinforced liquid crystal polymer used for injection molding. And it is very suitable for various demanding applications. Flame retardant grade V-0
6130LX Physical Property Table
Basic Information
Yellow card number E344082-100831264
Filler/reinforcement material glass fiber reinforcement material, 30% filler by weight
RoHS Compliance Contact Manufacturers
Processing method: Injection molding
Physical performance rating unit testing method
Density 1.66 g/cm3 ISO 1183
Shrinkage rate ISO 294-4
Vertical flow direction 0.60% ISO 294-4
Flow direction 0.12% ISO 294-4
Mechanical performance rating unit testing method
Tensile modulus 15000 MPa ISO 527-2/1A/1
Tensile stress (fracture) 145 MPa ISO 527-2/1A/5
Tensile strain (fracture) 2.0% ISO 527-2/1A/5
Bending modulus (23 ° C) 12800 MPa ISO 178
Bending stress (23 ° C) 220 MPa ISO 178
Compressive stress 133 MPa ISO 604
Test method for impact performance rating unit system
Impact strength of simply supported beam with notch ISO 179/1eA
-30°C 15 kJ/m2 ISO 179/1eA
23°C 15 kJ/m2 ISO 179/1eA
Simply supported beam without notch impact strength (23 ° C) 40 kJ/m2 ISO 179/1eU
Test method for thermal performance rating unit system
Hot deformation temperature (1.8 MPa, unannealed) 280 ° C ISO 75-2/A
Melting temperature 1 335 ° C ISO 11357-3
Linear coefficient of thermal expansion ISO 11359-2
Flow 5.0E-6 cm/cm/° C ISO 11359-2
Horizontal 6.2E-5 cm/cm/° C ISO 11359-2
Test method for unit system of rated electrical performance values
Surface resistivity>1.0E+15 ohms IEC 60093
Volume resistivity>1.0E+15 ohms · cm IEC 60093
Dielectric strength 34 kV/mm IEC 60243-1
Relative permittivity
1 MHz 4.00 IEC 60250
2.05 GHz 4.27 Internal Method
Dissipation factor
1 MHz 0.031 IEC 60250
2.05 GHz 6.0E-3 Internal Method
Leakage Trace Index 200 V IEC 60112
Test method for flammability rating unit system
UL flame retardant rating UL 94
0.750 mm V-0 UL 94
1.50 mm V-0 UL 94
Extreme Oxygen Index 51% ISO 4589-2
Injection rated value unit system
Drying temperature 150 ° C
Drying time 3.0 hours
Suggested moisture content of 0.010%
Hopper temperature 20.0 to 30.0 ° C
The temperature at the rear of the barrel is 335 to 345 ° C
The temperature in the middle of the barrel is 350 to 360 ° C
The temperature at the front of the barrel is 350 to 360 ° C
Spray nozzle temperature 350 to 360 ° C
Processing (melt) temperature 350 to 360 ° C
Mold temperature 80.0 to 120 ° C
Injection pressure 50.0 to 150 MPa
Maintain pressure between 50.0 and 150 MPa
Back pressure 0.00 to 3.00 MPa
AfterSalesService :
Key words:- Fiberglass reinforced LCP