Description :

　　LCP A115 American Tecona 15% fiberglass reinforcement

　　Chemical abbreviation in accordance with ISO 1043-1: LCP intrinsic flame retardancy meets FDA's UL 94 flame retardant testing, with a thickness of 0.44mm in natural color and black UL-Listing V-0 (black). According to the relative temperature index (RTI) of UL 746B, the electrical temperature is 240 ° C and the mechanical temperature is 220 ° C at 0.85mm.

　　Halogen-free; Flame retardant 15% glass fiber reinforcement.

　　A115 Physical Property Table

　　Basic Information

　　Yellow card number E83005-250993

　　Filler/reinforcement material glass fiber reinforcement material, 15% filler by weight

　　Characteristic halogen-free

　　flame retardancy

　　Institutional rating EU 2002/96/EC (WEEE)

　　FDA not rated

　　RoHS Compliance Contact Manufacturers

　　Processing method: Injection molding

　　Multipoint data Isothermal Stress vs. Strain (ISO 11403-1)

　　Resin ID (ISO 1043) LCP

　　Physical performance rating unit testing method

　　Density 1.50 g/cm3 ISO 1183

　　Shrinkage rate ISO 294-4

　　Vertical flow direction 0.40% ISO 294-4

　　Flow direction 0.10% ISO 294-4

　　Water absorption rate ISO 62

　　Saturation, 23 ° C 6.0E-3% ISO 62

　　Balance, 23 ° C, 50% RH 3.0E-3% ISO 62

　　Test method for hardness rating unit system

　　Rockwell hardness (M scale) 80 ISO 2039-2

　　Mechanical performance rating unit testing method

　　Tensile modulus 12000 MPa ISO 527-2/1A/1

　　Tensile stress (fracture) 200 MPa ISO 527-2/1A/5

　　Tensile strain (fracture) 3.1% ISO 527-2/1A/5

　　Bending modulus (23 ° C) 12400 MPa ISO 178

　　Bending stress (23 ° C) 250 MPa ISO 178

　　Compressive modulus 10000 MPa ISO 604

　　Compressive stress (1% strain) 85.0 MPa ISO 604

　　Test method for impact performance rating unit system

　　Simply supported beam notch impact strength (23 ° C) 42 kJ/m2 ISO 179/1eA

　　Simply supported beam without notch impact strength (23 ° C) 48 kJ/m2 ISO 179/1eU

　　Suspended wall beam notch impact strength (23 ° C) 45 kJ/m2 ISO 180/1A

　　Unscented Izod impact strength (23 ° C) 61 kJ/m2 ISO 180/1U

　　Test method for thermal performance rating unit system

　　Heat Deflection Temperature

　　0.45 MPa, Unanealed 250 ° C ISO 75-2/B

　　1.8 MPa, Unanealed 230 ° C ISO 75-2/A

　　8.0 MPa, Unanealed 157 ° C ISO 75-2/C

　　Vicat softening temperature 162 ° C ISO 306/B50

　　Melting temperature 1 280 ° C ISO 11357-3

　　Linear coefficient of thermal expansion ISO 11359-2

　　Flow 1.0E-5 cm/cm/° C ISO 11359-2

　　Horizontal 1.8E-5 cm/cm/° C ISO 11359-2

　　Test method for unit system of rated electrical performance values

　　Surface resistivity>1.0E+15 ohms IEC 60093

　　Volume resistivity 1.0E+15 ohms · cm IEC 60093

　　Dielectric strength 34 kV/mm IEC 60243-1

　　Relative permittivity IEC 60250

　　100 Hz 3.50 IEC 60250

　　1 MHz 3.00 IEC 60250

　　Dissipation factor IEC 60250

　　100 Hz 0.020 IEC 60250

　　1 MHz 0.018 IEC 60250

　　Internal method for arc resistance of 135 seconds

　　Leakage Trace Index 200 V IEC 60112

　　Test method for flammability rating unit system

　　UL flame retardant rating V-0 UL 94

　　Injection rated value unit system

　　Drying temperature 150 ° C

　　Drying time 4.0 to 6.0 hours

　　Suggested moisture content of 0.010%

　　Hopper temperature 20.0 to 30.0 ° C

　　The temperature at the rear of the barrel is 270 to 280 ° C

　　The temperature in the middle of the barrel is 275 to 285 ° C

　　The temperature at the front of the barrel is 280 to 290 ° C

　　Spray nozzle temperature 290 to 300 ° C

　　Processing (melt) temperature 285 to 295 ° C

　　Mold temperature 80.0 to 120 ° C

　　Injection pressure 50.0 to 150 MPa

　　Fast injection speed

　　Maintain pressure between 50.0 and 150 MPa

　　Back pressure 0.00 to 3.00 MPa