Electronic product special material LCP G-930 American Amoco high strength flame retardant
Category:
Rubber and plastic/engineering plastic/LCP
Model:
Brand:
Amoco, USA
Retail Price
80.00USD
重量
kg
- Product Description
-
Description :
LCP G-930, an American Amoco G-930 liquid crystal polymer (LCP), is a glass fiber reinforced injection grade material developed specifically for electronic/electrical products, using surface mount technology. The molding performance of this resin. Even when the mold temperature is below 200 ° F (93 ° C), Xydar G-930 rarely or never produces overflow during long-distance flow filling of ultra-thin wall components. In addition, the molded products have low warpage and excellent welding line strength. Even at high temperatures, this material has high strength and stiffness, low thermal expansion coefficient, high flexural temperature, inherent flame retardancy, excellent resistance to most chemicals, as well as weather resistance and radiation resistance.
Characteristics: Low curvature and warping; High rigidity; High intensity; Flame retardant; Weather resistance; Chemical resistance; Good formability
Application: Electrical/electronic application field; Electrical components; Industrial components; Industrial applications; Automotive electronics; Applications in the automotive field
G-930 Physical Property Table
Basic Information
Yellow card number E95746-101203201
Filler/reinforcement material glass fiber reinforcement material, 30% filler by weight
Low warpage characteristic
Rigid, high
high-intensity
Anti gamma radiation
Good formability
Good chemical resistance
Good weather resistance performance
flame retardancy
Usage: Electrical/Electronic Application Field
electrical components
Industrial components
industrial applications
Automotive Electronics
Applications in the automotive field
spool
RoHS Compliance RoHS Compliance
Appearance black
natural color
Formal particle
Processing method: Injection molding
Multi point data viscosity vs. Shear Rate (ISO 11403-2)
Physical performance rating unit testing method
Specific gravity 1.60 g/cm3 ASTM 792
Water absorption rate (24 hours)< 0.10 % ASTM 570
Mechanical performance rating unit testing method
Tensile modulus 15900 MPa ASTM 638
Tensile strength 135 MPa ASTM 638
Elongation (at break) 1.6% ASTM 638
Bending modulus 13400 MPa ASTM 790
Bending strength 172 MPa ASTM 790
Test method for impact performance rating unit system
Suspended wall beam notch impact strength 96 J/m ASTM 256
Unscented cantilever beam impact 430 J/m ASTM 4812
Test method for thermal performance rating unit system
Thermal deformation temperature under load
1.8 MPa, Unanealed 274 ° C ASTM 648
1.8 MPa, Unanealed 282 ° C ISO 75-2/A
Ball Pressure Test 1(270°C, 3.00 mm) Pass IEC 60695-10-2
Linear thermal expansion coefficient ASTM 696
Flow from 3.6E-6 to 7.2E-6 cm/cm/° C ASTM 696
Horizontal 4.0E-5 to 7.9E-5 cm/cm/° C ASTM 696
RTI Elec (0.750 mm) 220 °C UL 746
RTI Imp (0.750 mm) 200 °C UL 746
RTI (0.750 mm) 220 °C UL 746
Test method for unit system of rated electrical performance values
Volume resistivity 1.0E+16 ohms · cm ASTM 257
Dielectric strength (1.57 mm) 39 kV/mm ASTM 149
Dielectric constant ASTM 150
60 Hz 4.20 ASTM 150
1 MHz 3.90 ASTM 150
Arc resistance 2>300 sec UL 746
Leakage Traceability Index 185 V ASTM 3638
Test method for flammability rating unit system
UL flame retardant rating 3 (0.400 mm, black) V-0 UL 94
Injection rated value unit system
Drying temperature 149 ° C
Drying time 6.0 to 8.0 hours
Processing (melt) temperature 321 to 360 ° C
Mold temperature 65.6 to 93.3 ° C
Locking force 2.8 to 5.5 kN/cm2
Screw aspect ratio 20.0: 1.0 to 24.0: 1.0
Screw compression ratio of 2.5:1.0 to 3.0:1.0
AfterSalesService :
Key words:- Electronic product specific material LCP